產品說明Product description

·TA75C-22是一款高性能材料，具有非常強勁的包膠粘接強度和特別舒適的手感。可快速成型。

·TA75C-22is a kind of high performance material which has very strong adhesive strength and special comfortable touch.Also it can be taken shape rapidly.

關鍵特性Key characteristic

1.表面啞，手感細膩爽滑。Dumb surface, the handle is exquisite and smooth

2.粘接強度非常高,可粘接材質:ABS.PC TPU。Very high bonding strength, adhesive materials：ABS,PC,TPU.

3.成型快、不粘模具。Rapid molding，non-stick mold

4.表面耐刮擦，不易起毛屑。Scratch resistance on the surface,not easy to fluff

功能Function

產品應用

Main application

手機保護Phone protective cover

電腦Computer

儀器外殼Instrument shell

電子器件粘膠配件Electronic plastic accessories

加工方法Processing method

1 注塑成型Injection molding     2 擠出成型Extrusion molding

環保認證

Environmental certification

ROHS

REACH

EN71-3

PAHS

ASTM-F963

Phthalate

顏色Color

本色 Natural

氣味Smell

少許樹脂味A little resin smell

外型Appearance

圓球形小顆粒Cylindrical particle，about 3mm×1.5mm

儲藏期Storage period

常溫下通風干燥，24個月Ventilated dry at normal temperature，about 24 months

包裝方式Packaging method

25公斤/袋 25kg/bag

物理性能Physical properties

結果Result

單位Unit

方法Method

成型條件Molding condition

比重Specific gravity

1.2±0.02

g/cm3

ASTM D792

干燥溫度Drying temp       90℃

硬度Hardness

75±5

shoreA

ASTM D2240

干燥時間Drying time     2Hours

拉伸強度Tensile strength

>8

Mpa

ASTM D412

射嘴溫度Nozzle temp      190℃

斷裂延伸Elongation at break

>400

%

ASTM D412

螺筒一段溫度Screw 1 temp 180℃

撕裂強度Tearing strength

>40

Kn/m

ASTM D624

螺筒二段溫度Screw 2 temp 170℃

熔融指數Melt index

>15

g/10min

ASTM D1238

螺筒三段溫度Screw 3 temp 160℃

注意事項Matters need attention

清洗料管

Purge compound

需使用PP或 PE清洗干凈機臺螺桿，且把機臺射嘴清除干凈please make sure you that you have cleaned the machine screw with PP or PE, and put the machine nozzle thoroughly clean

著色

Coloring

請選擇以PE或EVA為基材之色母，切勿使用以PVC為基材者。另外加工時請采用較高的螺桿轉速和較高的背壓，才能讓著色劑達到較好的分散效果Please select color master batch on PE or EVA material with the exception of PVC.Higher screw speed and backpressure and needed for better colorant dispersion

回收Recycling

二次料（水口料）回收比率建議最多10%。Consistent regrind usage of up to 10% is permissible